| SEM-VIEW | |
 | |
| GRADE DATA | |
| Fe （%） | 90 |
| Cu （%） | 10 |
| Theoretical Density（g/cm3） | 7.97 |
| H2-Loss（%） | ≤0.65 |
| Apparent Density（g/cm3） | 0.5-0.7 |
| Tap Density（g/cm3） | 0.8-1.0 |
| D10 Laser（um） | 3.0-6.0 |
| D50 Laser（um） | 17.0-20.5 |
| D90 Laser（um） | 60.0-64.5 |
| Hardness/Bending Strength-Temperature Curve |
 |
| Density-Temperature Curve |
 |
Product Features:
Large surface area, high activity, low sintering temperature, high density, high hardness sintered (maximum 102HRB) good sintering stability, bending strength up to1534Mpa, good flowability.
Main Application:
Based powder of diamond tools matrix, effectively decreasing the sintering temperature, improving the uniformity of the sintering organizations, increasing the grip strength.